Título : Cellulose Extraction For Sport Clothing.
Autor : Alexis, Frank
Gushque Lamiña, Edison Fernando
Palabras clave : Cellulose
Fibers
Cellulosic membranes
Textile
Manufacture
Celulosa
Fibras
Membranas De Celulosa
Textiles
Manufactura
Fecha de publicación : jul-2020
Editorial : Universidad de Investigación de Tecnología Experimental Yachay
Resumen : Doce muestras de flora ecuatoriana fueron para fabricar membranas de celulosa y compararlas con fibras textiles usadas en la ropa deportiva. Se diseñó la metodología de extracción para obtener una concentración apropiada de celulosa al 40%. Las muestras fueron caracterizadas por XDR, DSC y FTIR y comparadas con la celulosa comercial. Después su procesamiento a membranas de celulosa usando un método en DMAc/LiCl y calentamiento. La coagulación en agua fue realizada para incrementar la estabilidad de la membrana. Las caracterizaciones (tasa de enfriamiento, recaptura de humedad y XRD) nos permitieron establecer similitudes y diferencias con las fibras sintéticas (nylon, poliéster y algodón). Luego, se usaron se aplicaron métodos estadísticos para clasificar los datos en tres grupos. Un grupo poseía altas propiedades de retención de agua, el segundo posee propiedades similares a las fibras textiles sintéticas, mientras que el último grupo poseía características similares a la celulosa comercial. Los datos sugieren no correlación entre el índice de cristalinidad, recaptura de humedad y tasa de enfriamiento. Otros factores, tales como el grado de polimerización y el peso molecular abrirán nuevos tópicos importantes en la presente investigación para la fabricación de productos de valor agregado.
Descripción : Twelve samples of the Ecuadorian flora were selected to be studied for the fabrication of cellulosic films and to compare their properties with synthetic textile fibers used in sport-clothing. An extraction methodology was designed to obtain an appropriate cellulose concentration of 40%. Samples were characterized using XRD, DSC, and FTIR and compared with the commercial cellulose. The samples were then processed to cellulosic films by using DMAc/LiCl method under heating. An additional coagulation step was performed after the film formation to enhance the stability. The characterizations of the films (cooling rate, moisture regain, and XRD) allowed us to compare samples and establish similarities and differences between them and synthetic fibers (nylon, polyester, and cotton). Then, applied statistical methods were used to classify data into three groups. One group offers high water-intake properties, the second possesses comparable properties to synthetic textile fibers whereas the last one shows similar features to commercial cellulose. The data suggests no correlation between the crystallinity index, moisture-regain and cooling rate. Other factors, such as the degree of polymerization and molecular weight, will open new important avenues for the current research for the fabrication of value-added products.
URI : http://repositorio.yachaytech.edu.ec/handle/123456789/166
Aparece en las colecciones: Biomedicina

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
ECBI0020.pdf2.07 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.